Einfluss der Temperatur auf das Fließverhalten von P92 Blechmaterial unter quasistatischer Zugbeanspruchung

摘要

The relatively new ferritic martensitic steel P92 (NF616) has been developed for the application in power plants. Because of its high creep resistance the material is used as pipe material, which means as thick-walled part. Within the scope of the Collaborative Research Center 561 of Aachen University of Technology P92 is planed to use as sheet metal as a component of a sandwich structure for cooling thermal high loaded parts of a steam turbine. Single segments of this cooling structure were formed by die bending into the demanded shape. Therefore it is necessary to investigate the flow behaviour as a function of temperature for this material in combination with a mathematical model. In this work quasi static tensile tests in the temperature range between 293K and 973K were performed and the results were described as a function of temperature.%Der relativ neue ferritisch-martensitische Stahl P92 (NF616) wurde hauptsächlich für den Einsatz im Kraftwerksbau entwickelt. Auf Grund seiner hohen Kriechbeständigkeit wird dieser Stahl vorrangig als Rohrleitungswerkstoff, also als dickwandiges Bauteil, verwendet. Im Sonderforschungsbereich 561 an der RWTH Aachen ist geplant, diesen Werkstoff in Form von Blechmaterial als Einzelkomponente einer sandwichartigen Kühlstruktur zur Kühlung thermisch hochbelasteter Bauteile innerhalb der Dampfturbine zu verwenden. Einzelne Segmente dieser Kühlstruktur werden mittels Gesenkbiegen in die gewünschte Gestalt umgeformt. Hierfür ist es notwendig, das Fließverhalten in Abhängigkeit der Temperatur dieses Werkstoffes zu kennen und mathematisch beschreiben zu können. In dieser Arbeit wurden quasistatische Zugversuche im Temperaturbereich von 293K bis 973K durchgeführt und die Ergebnisse in Abhängigkeit der Temperatur modelliert.