Korrosion Thermisch Gespritzter Schichten Auf Der Basis Von Aluminiumoxid

摘要

In this paper, the results of corrosion investigations performed on thermally sprayed coatings with different compositions in the Al_2O_3-TiO_2 system (Al_2O_3, Al_2O_3-3 %TiO_2, Al_2O_3-40 %TiO_2, Al_2 TiO_5) are presented. The coatings were deposited on corrosion-resistant stainless steel substrates using APS and HVOF processes. The coatings were characterized by means of optical microscopy and SEM of metallographically prepared cross sections as well as surfaces before and after corrosion testing. The changes in phase composition occurring during spraying were studied by X-ray diffraction. The corrosion experiments were performed with 1 N solutions of NaOH and H_2SO_4 at room temperature, 60 ℃, and 85 ℃. In contrast to expectations, APS-sprayed coatings were found to be more corrosion-resistant than the denser HVOF-sprayed coatings were.%In dieser Arbeit werden Untersuchungsergebnisse zur Korrosion thermisch gespritzter Schichten aus dem System Al_2O_3/TiO_2 (Al_2O_3, Al_2O_3-3%TiO_2, Al_2O_3-40 %TiO_2 und Al_2TiO_5) vorgestellt. Die Proben wurden durch Spritzen mit ÄPS und HVOF auf Substrate aus einem korrosionsbeständigen Stahl hergestellt. Die Charakterisierung der Schichten erfolgte an metallographischen Querschliffen am Lichtmikroskop und am REM bzw. an den Probenoberflächen vor und nach den Korrosionsuntersuchungen. Für die quantitative Bestimmung der Schichtporosität müssen REM-Aufnahmen verwendet werden. Die Veränderungen der Phasenzusammensetzungen durch den Spritzprozess wurden röntgenogra-phisch untersucht. Die Korrosionsversuche wurden in Natriumhydroxid und Schwefelsäure (jeweils in IN Lösung) bei Raumtemperatur, 60 ℃ und 85 ℃ durchgeführt. Entgegen den Erwartungen erwiesen sich APS-gespritzte Schichten als deutlich korrosionsbeständiger als HVOF-gespritzte.