Untersuchung Des Erosionsverhaltens Von Silberbasierten Kontaktwerkstoffen Mittels Fib-techniken

摘要

The understanding of the degradation mechanisms of contact materials is a key issue for the development of new materials with enhanced durability. This can be achieved through the investigation of the microstructure modification caused by electrical arcs on the surface of contacts. In this work, the erosion behaviour of pure silver and silver based composites as well as the characterization in two or three dimensions is presented. Single breaking operations were performed with direct current. Using white light interferometry, the size of the craters on the surface as well as the volume of eroded material has been measured. By means of dual beam techniques, the microstructural modifications in the crater have been investigated and reconstructed in three dimensions.%Für das Verständnis der Schädigungsmechanismen von Kontaktwerkstoffen und die Entwicklung neuartiger Materialien ist die korrekte Darstellung und Analyse der Gefügesituation von essentieller Bedeutung. Dieses Verständnis erreicht man durch Untersuchung der Mikrostrakturveränderungen auf und unter der Oberfläche, die durch einen Lichtbogen verursacht wurden. In dieser Arbeit wird sowohl das Erosionsverhalten von reinem Silber und Silber-Metalloxid-Kompositen, als auch die Charakterisierung in zwei und drei Dimensionen besprochen. Einzelschaltungen unter Gleichstrombedingungen wurden durchgeführt und analysiert. Die Kratertopographie wurde mit Hilfe eines Weißlichtinterferometers vermessen und das bewegte Volumen berechnet. Mit Hilfe der Dual-Beam Techniken wurden die Schaltkrater ober- und unterhalb der Oberfläche untersucht, sowie dreidimensional rekonstruiert.