Influence of anodic oxide coatings on screwing behaviour and susceptibility to stress corrosion cracking of self-tapping aluminium screws

摘要

Enhanced use of lightweight materials, namely aluminium and magnesium, requires the application of appropriate production techniques. Self-tapping screws represent an innovative joining technology. High-strength aluminium alloys can be used as screw material. Stringent requirements regarding the wear resistance of screw surfaces result from the thread-forming process. These requirements are met by oxide ceramic conversion layers produced by hard anodizing. Based on application-oriented testing methods, the influence of hard anodized layers on the screwing behaviour and susceptibility to stress corrosion cracking of high-strength aluminium screws is examined.%Durch den zunehmenden Einsatz von metallischen Leichtbauwerkstoffen wie Aluminium oder Magnesium entsteht der Bedarf nach angepassten Fertigungsverfahren. Gewindefurchende Schrauben stellen ein innovatives Fügekonzept dar. Als Schraubenwerkstoff k?nnen dabei hochfeste Aluminiumlegierungen zum Einsatz kommen. Jedoch resultieren aus dem Prozess des Gewindefurchens erh?hte Anforderungen an die Verschlei?best?ndigkeit der Schraubenoberfl?che. Diesen Anforderungen kann mit hartanodisierten oxidkeramischen Konversionsschichten auf der Schraubenoberfl?che begegnet werden. Die vorliegende Untersuchung bewertet auf Grundlage praxisnaher Prüfungen den Einfluss der Oxidschichten auf das Einschraubverhalten sowie auf die Empfindlichkeit hochfester Aluminiumschrauben gegenüber Spannungsrisskorrosion.