Performance of alloy 800H for high-temperature heat exchanger applications

摘要

The tensile properties of austenitic Alloy 800H have been evaluated at temperatures ranging from ambient to 1000℃. The results indicate that the tensile strength was gradually reduced with increasing temperature. Between ambient temperature and 200℃, the failure strain was reduced possibly due to the occurrence of dynamic strain aging followed by its enhancement at temperatures up to 500℃. Alloy 800H did not exhibit any failure in an acidic solution at constant-load. However, the true failure stress in this environment was reduced at elevated temperatures under a slow-strain-rate condition. The magnitude of electrochemical potentials became more active with increasing temperature. A detrimental effect of more noble controlled potential on the cracking susceptibility was noted in terms of the true failure stress. A combination of ductile and intergranular brittle failures was seen in the primary fracture surface of the tested cylindrical specimens.