Electron microscopy and hardness study of a semi-solid processed 27 wt%Cr cast iron

摘要

A semi-solid processed 27 wt%Cr cast iron was studied by electron microscopy and its microstructure was related to the hardness. In the as-cast condition, the primary proeutectic austenite was round in shape while the eutectic M_7C_3 carbide was found as radiating clusters mixed with directional clusters. Growth in the [001]M_7C_3 with planar faces of {020}M_7C_3 and {240}M_7C_3 was usually observed with an encapsulated core of austenite. Destabilisation heat treatment followed by air cooling led to a precipitation of secondary M_(23)C_6 carbide and a transformation of the primary austenite to martensite in the semi-solid processed iron. Precipitation behaviour is comparable to that observed in the destabilisation of conventional cast iron. However, the nucleation of secondary M_(23)C_6 carbide on the eutectic M_7C_3 carbide was observed for the first time. Tempering after destabilisation led to further precipitation of carbide within the tempered martensite in the eutectic structure. The maximum hardness was obtained after destabilisation and tempering heat treatment due to the precipitation of secondary carbides within the martensite matrix and a possible reduction in the retained austenite.