Effect of annealing on microstructure and mechanical properties of bulk nanocrystalline Fe3Al alloy with 5 wt.% Cu prepared by aluminothermic reactic

摘要

Micrqstructure and mechanical properties of bulk nanocrystalline Fe3Al based alloy with 5 wt.% Cu prepared by aluminothermic reaction before and after annealed at 873, 1073 and 1273 K for 8 h were investigated. Microstructures of the alloy before and after the annealing consisted of a Fe-Al-Cu matrix, a little AI2O3 sphere and Fe3AlCx fiber phases. The matrix of the alloy before the annealing was composed a nanocrystalline phase with disordered bcc crystal structure and a little amorphous phase. The amorphous phase disappeared after the annealing and Fe3 Al phase with ordered DO3 structure appeared in the alloy after annealed at 1073 and 1273 K in the matrix of the alloy. Size of the Fe3 A1Q fiber phase increased with the annealing temperature. The alloy after the annealing had better plasticity, higher yield strength than that of the alloy before the annealing, and the alloy after annealed at 1273 K had the highest yield strength.