机译:2198-T8 Al-Li合金接头摩擦搅拌熔核的力学性能和疲劳裂纹扩展速率
School of Aeronautics, Northwestern Polytechnical University, Xi'An, PR China;
School of Aeronautics, Northwestern Polytechnical University, Xi'An, PR China;
School of Aeronautics, Northwestern Polytechnical University, Xi'An, PR China;
School of Materials, Northwestern Polytechnical University, Xi'An, PR China;
Friction stir welded nugget; 2198-T8 Al-Li alloy; Fatigue crack growth rate; Residual stress; R ratio;
机译:搅拌摩擦焊接2198-T8 Al-Li合金接头的残余应力效应和疲劳行为
机译:搅拌摩擦焊接2198-T8 Al-Li合金的组织与力学性能的相关性
机译:搅拌摩擦焊接2198-T8 Al-Li合金接头搅拌区异常断裂的起源
机译:残余应力对摩擦搅拌磨损2198-T8和2195-T8 Al-Li合金接头疲劳裂纹谱的影响
机译:用相似和不同的铝合金制造的搅拌摩擦焊接接头的力学性能和微观结构的研究。
机译:5A06合金超薄板搅拌摩擦焊接对接头的组织演变和力学性能。
机译:Al 2024 T351合金搅拌摩擦T型接头疲劳裂纹扩展的数值模拟。
机译:al-Li 2195母金属,可变极性等离子弧焊和摩擦搅拌焊缝的疲劳裂纹扩展速率测试结果