Reactive brazing of Al alloy to Mg alloy using zinc-based brazing alloy

摘要

According to the feature of Mg-Zn eutectic reaction, Al alloy was bonded to Mg alloy by contact reaction brazing using a zinc-based brazing alloy successfully. The experimental observations showed that Mg-Al intermetallic compounds were avoided for the addition of the zinc-based brazing alloy. The Mg substrate and the remanent brazing alloy were bonded with the reaction zone that formed along the zinc rich and magnesium poor interface. Only a few Mg-Zn intermetallic compounds (MgZn2) existed homogeneously in the reaction zone. The substrate and the remanent brazing alloy were bonded with a thin Al-Zn solution. The average tensile-shear strength of the final joints was a little lower than that of the zinc-based brazing alloy owning to some pores at the interface between the reaction zone and the remanent brazing alloy layer.