Effect of post weld heat treatments on microstructure and mechanical properties of friction stir welded joints of Al-Zn-Mg alloy AA7039

摘要

Friction stir welded joints of Al-Zn-Mg aluminum alloy AA7039 were given five different post weld heat treatments in order to investigate their effect on microstructure and mechanical properties. In general, all the applied post weld heat treatments increased the size of α aluminum grains in all zones of friction stir weld joints. Abnormal grain growth was observed in entire zone modified by friction stir welding in case of solution treated joints with and without artificial aging. The naturally aged joints offered the highest mechanical properties while solution treated joints offered lowest mechanical properties of the joints. Naturally aged joints yielded highest tensile strength (94.9%) and elongation (174.2%) efficiencies while artificially aged joints yielded highest yield strength efficiency (96.7%). Further, post weld heat treatment also affected fracture location and mode of fracture.