Boron nitride nanoplatelets as two-dimensional thermal fillers in epoxy composites: new scenarios at very low filler loadings

摘要

Hexagonal boron nitride (h-BN) nanoplatelets (0.6 mu m in diameter and 100 nm in thickness) are introduced into epoxy resin to improve the polymer's thermal conducting ability. As expected, the thermal conductivities (TCs) of the composites, especially the in-plane TCs, are significantly increased. The in-plane TC of the epoxy composites can reach 1.67 W/mK at only 0.53 wt% loading, indicating h-BN nanopletelets are very effective thermal fillers. However, after carefully studied the correlation of the TC improvement and filler content, a sudden drop of the TC around 0.53 wt% filler loading is observed. Such an unexpected decrease in TC has never been reported and is also found to be consistent with the T-g changes versus filler content. Similar trend is also observed in other 2-D nanofillers, such as graphene oxide, reduced graphene oxide, which may indicate it is a general phenomenon for 2-D nanofillers. SEM results suggest that such sudden drop in TC might be coming from the enrichment of these 2-D nanofillers in localized areas due to their tendency to form more ordered phase above certain concentrations.