PALS Free Volume Study of Dry and Water Saturated Epoxies

摘要

Free volume cavity sizes and fractions of epoxy specimens were determined using positron annihilation lifetime spectroscopy (PALS). PALS data were obtained before and after specimen water equilibration. Specimens were bisphenol A epoxide (B) and/or glycol epoxide (G) cured with a polyamide. Free volume sites increased linearly and cavity sizes decreased linearly with epoxide B:G ratio. Glass transition temperature (T_g) increased with epoxide B:G ratio. Water molecules in wet epoxy B filled approximately six percent of the cavities, epoxy G cavity size increased 11.4% after water equilibrium and was ascribed to cavity expansion. PALS results differed for commercial corrosion inhibitors in wet and dry mixtures of these epoxides.%Fueron determinados los volúmenes libres de las cavidades "porosidad" y la fracción de grupos epóxicos usando espectroscopia del tiempo de vida de aniquilación de I positrón (PALS). Los datos PALS fueron obtenidos antes y después de que la muestra se encontraba en equilibrio con el agua. Las muestras fueron exóxicos (B) tipo bisfenol A y/o epoxi glicol (G) curados con una poliamida. Los espacios libre se incrementan linealmente y el tamaño de las cavidades disminuye linealmente con la relación epoxica (B):(G). La temperatura de transición vitrea (T_g) se incrementa con la relación epóxida. (B):(G). Las moléculas de agua llenan aproximandamente 316% de las cavidades del epóxico (B). El tamaño de las cavidades en el epóxico (G) se incrementan en 11.4% después de que se obtiene equilibrio con el agua y fue atribuida a la expansión de las cavidades. Los resultados obtenidos con el método PALS difieren para los inhibidores comerciales de corrosión en mexclas húmedas y secas de esos epoxidos.