Basic analysis of weldability and machinability of structural materials for ITER Toroidal Field coils

摘要

A manufacturing study has been conducted to examine the welding and machining capabilities for strengthened austenitic stainless steels with a high nitrogen content, JJ1 and ST-SS316LN, to be employed for ITER Toroidal Field (TF) coil structural components. It was found that the applicable EB welding condition for JJ1 was limited to up to 40 mm thick plates. A wider range of welding conditions was found in the vertical upward direction. Based on those results, a verification test up to 900 mm in length was successfully conducted. With respect to TIG welding, an average deposition rate of 26 g/min (i.e. the filler wire supplying speed of 3000 mm/min) was achieved. In addition to the welding tests, a series of machining tests has been conducted to examine the machinability of JJ1 and ST-SS316LN. Various types of machining tools were examined. In practical application, the cutting speed should be low to extend the tool life. At a cutting speed of 40 m/min, a tool life of more than 2 h (at a traveling distance of up to 9 m) was attained. The degree of cutter wear after 30 min of operation, at a cutting speed of 40 m/min, was found to be around 0.1 mm, which is within an acceptable range.