Effect of relative humidity on some physical and mechanical properties of different types of fibreboard

摘要

Equilibrium moisture content and strength properties as a function of relative humidity (RH) were measured in three types of commercial fibreboards with different densities. The measurements were made after specimens had been conditioned to equilibrium at 35, 50, 65, 80 and 95% RH and 20 °C. It was shown that the modulus of elasticity decreased slightly between 35 and 65% RH and markedly – at above 65% RH for all types of boards. A very strong decrease of modulus of elasticity was observed at about 80% RH (capillary condensation). A similar decreasing trend was observed in bending strength. Overall, high RH had a noticeably detrimental effect both on the MOE and the bending strength for all tested boards. Adequate correlation exists between bending MOE and bending strength with moisture content. The lower the density of boards the higher their equilibrium moisture content. An industriell im Trockenverfahren gefertigten Faserplatten mit unterschiedlicher Rohdichte wurden im variablen Klima bei 20 °C und 35, 50, 65, 80 und 95% rel. Luftfeuchte der Biege-E-Modul und die Biegefestigkeit bestimmt. Im Bereich bis zu 65% rel. Luftfeuchte sinken Biegefestigkeit und E-Modul leicht ab. Insbesondere oberhalb von 80% rel. Luftfeuchte kommt (also im Bereich der Kapillarkondensation) es zu einem starken Abfall der Biegefestigkeit und des E-Moduls. Zwischen dem Feuchtegehalt und den genannten Eigenschaften besteht eine lineare Korrelation. Je geringer die Rohdichte ist, umso höher ist die Gleichgewichtsfeuchte. Hierbei ist allerdings eine Überlagerung des Einflusses des Klebstoffanteils vorhanden.