Oxidation Of Carbon Oxide Over Monolithic Platinum Catalysts Doped With Metal Oxides

摘要

The deposition of NiO, MnO, CeO_2, Co_3O_4 or Fe_3O_4 onto the surface of an Al_2O_3-based wash-coat enhances the activity of the 0.15% Pt/Al_2O_3 catalyst in CO oxidation. The highest activities were found to be those of the 0.15% Pt/0.1 % Mn/Al_2O_3 and 0.15% Pt/0.1 % Ce/Al_2O_3 catalysts, over which a 100% conversion of CO was achieved at 204 ℃ and 209 ℃, respectively. The activity of 0.15% Pt/Al_2O_3, as well as that of the oxide-doped 0.15% Pt/MO_x/Al_2O_3 (M = Ni, Mn, Ce, Co, Fe) catalysts, can be notably increased by using Pt(NO_3)_4 as a Pt precursor instead of H_2PtCl_6.%Naniesienie na powierzchnię warstwy pośredniej z Al_2O_3 tlenków: NiO, MnO, CeO_2, Co_3O_4, Fe_3O_4 podwyższa aktywność katalizatora 0,15% Pt/Al_2O_3 w utlenianiu CO. Najwyższą aktywność w utlenianiu CO wykazują katalizatory 0,15% Pt/0,1% Mn/Al_2O_3 i 0,15% Pt/0,1% Ce/Al_2O_3, na których 100% przere-agowania CO uzyskano odpowiednio w temperaturach 204 ℃ i 209 ℃. Znaczny wzrost aktywności katalizatora 0,15% Pt/Al_2O_3 oraz katalizatorów 0,15% Pt/MO_x/Al_2O_3 (M = Ni, Mn, Ce, Co, Fe) z dodatkiem tlenków uzyskuje się, stosując jako prekursor platyny Pt(NO_3)_4 zamiast H_2PtCl_6.