The Solubility of MoO_3 in Aqueous Solutions of HClO_4 at T= 300℃ and P = 100 bar by Experimental Data

T. P. Dadze; G. A. Kashirtseva; M. P. Novikov; A. V. Plyasunov; Yu. B. Shapovalov

首页> 外文期刊>Doklady Earth Sciences >The Solubility of MoO_3 in Aqueous Solutions of HClO_4 at T= 300℃ and P = 100 bar by Experimental Data

【24h】

The Solubility of MoO_3 in Aqueous Solutions of HClO_4 at T= 300℃ and P = 100 bar by Experimental Data

机译：实验数据表明MoT_3在HClO_4水溶液中在T = 300℃和P = 100 bar时的溶解度

获取原文

获取原文并翻译 | 示例

获取外文期刊封面封底 >>

开具论文收录证明 >>

文献代查 >>

团队文献服务 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

The solubility of crystalline MoO_3 in aqueous solutions of HClO_4 at T= 300℃ and P = 100 bar was determined in experiments. It was shown that the acidity of the solution is the determining factor of the solubility of molybdenum trioxide under hydrothermal parameters. The formation constant was calculated for the HMoO_4~- neutral complex (pK_0 = 3.50 ± 0.20).

机译：实验确定了MoO_3晶体在HCl = 4的水溶液中在T = 300℃和P = 100 bar时的溶解度。结果表明，溶液的酸度是水热参数下三氧化钼溶解度的决定因素。计算出HMoO_4-中性复合物的形成常数（pK_0 = 3.50±0.20）。

著录项

来源
《Doklady Earth Sciences 》 |2014年第1期| 548-549| 共2页
作者
T. P. Dadze; G. A. Kashirtseva; M. P. Novikov; A. V. Plyasunov; Yu. B. Shapovalov;
展开▼
作者单位

Institute Experimental Mineralogy, Russian Academy of Sciences, Chernogolovka, Russia;

Institute Experimental Mineralogy, Russian Academy of Sciences, Chernogolovka, Russia;

Institute Experimental Mineralogy, Russian Academy of Sciences, Chernogolovka, Russia;

Institute Experimental Mineralogy, Russian Academy of Sciences, Chernogolovka, Russia;

Institute Experimental Mineralogy, Russian Academy of Sciences, Chernogolovka, Russia;

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类
关键词

相似文献

外文文献
中文文献
专利

1. Iron(III) solubility and speciation in aqueous solutions. Experimental study and modelling: Part 1. Hematite solubility from 60 to 300 deg C in NaOH-NaCl solutions and thermodynamic properties of Fe(OH)_4-(aq) [J] . Igor I. Diakonov, Jacques Schott, Francois Martin, Geochimica et Cosmochimica Acta: Journal of the Geochemical Society and the Meteoritical Society . 1999 ,第15期

机译：铁（III）在水溶液中的溶解度和形态。实验研究和建模：第1部分。赤铁矿在NaOH-NaCl溶液中从60到300摄氏度的溶解度和Fe（OH）_4-（aq）的热力学性质
2. Carbon dioxide solubility in aqueous solutions of sodium chloride at geological conditions: Experimental results at 323.15, 373.15, and 423.15 K and 150 bar and modeling up to 573.15 K and 2000 bar [J] . Zhao Haining, Fedkin Mark V., Dilmore Robert M., Geochimica et Cosmochimica Acta: Journal of the Geochemical Society and the Meteoritical Society . 2015 ,第Null期

机译：地质条件下二氧化碳在氯化钠水溶液中的溶解度：在323.15、373.15和423.15 K和150 bar下的实验结果，以及高达573.15 K和2000 bar的模型
3. Zinc complexation in aqueous sulfide solutions: Determination of the stoichiometry and stability of complexes via ZnS(cr) solubility measurements at 100 degrees C and 150 bars [J] . Tagirov BR, Suleimenov OM, Seward TM Geochimica et Cosmochimica Acta: Journal of the Geochemical Society and the Meteoritical Society . 2007 ,第20期

机译：硫化水溶液中的锌络合：通过在100摄氏度和150巴下进行ZnS（cr）溶解度测量来确定络合物的化学计量和稳定性
4. Saturation Dislocation Microstructures In A Copper Single Crystal During Fatigue In HClO_4 Aqueous Solution [C] . J H Yang, X P Zhang, Y -W Mai International Conference on Structural Integrity and Fracture . 2004

机译：HClO_4水溶液疲劳期间铜单晶饱和脱位微结构
5. MUTUAL SOLUBILITIES OF PYRITE, PYRRHOTITE, QUARTZ, AND GOLD IN AQUEOUS SODIUM-CHLORIDE SOLUTIONS FROM 200 DEGREES TO 500 DEGREES C, AND 500 TO 1500 BARS, AND GENESIS OF THE CORTEZ GOLD DEPOSIT, NEVADA. [D] . RYTUBA, JAMES JOHN -1

机译：黄铁矿，黄铁矿，石英和金在200℃至500℃，500到1500巴的氯化钠水溶液中的互溶性，以及内华达州科尔特斯金矿的成因。
6. Experimental data on the removal of acid orange 10 dye from aqueous solutions using TiO [O] . Behzad Rahimi, Nayereh Rezaie-Rahimi, Negar Jafari, 2021

机译：使用TiO从水溶液中除去酸橙10染料的实验数据
7. Mechanical properties of various concrete after high temperature exposure Mechanical property of various types of concrete after high temperature exposure is investigated. Considering compressive strength requirement for a vertical element in high rise building, concrete specimens with various design strengths of 35, 80, 100, and 150 MPa were tested. Particularly, the influence of incorporated steel fiber on fire resistance is of interest in this study. Experimental results show that the fire resistance depends on the design strength and steel fiber content. Normal strength concrete (NSC) of a design strength of 35 MPa or high performance concrete (HPC) of 80-100 MPa does not spall when exposed to 100-400 °C of temperature. However, an explosive spalling occurs at 300 °C when the HPCs contain 1 vol. of steel fiber. Ultra-high performance concrete (UHPC) of a design strength of 150 MPa and 1.5 vol. of steel fiber also shows dramatic spalling at 300 °C. The experimental results found in this study can contribute to a better understanding of the behaviors of HPC and UHPC under fire and the role of steel fiber on the fire resistance. [O] . 2017

机译：研究了高温暴露后各种混凝土高温曝光机械性能各种混凝土的机械性能。考虑到高层建筑中垂直元件的抗压强度要求，测试了35,80,100和150MPa各种设计强度的混凝土试样。特别是，在这项研究中，掺入钢纤维对耐火性的影响。实验结果表明，耐火性取决于设计强度和钢纤维含量。在暴露于100-400°C的温度时，80-100MPa的设计强度为35MPa或高性能混凝土（HPC）的正常强度混凝土（NSC）不会击落。然而，当HPC含有1体积的钢纤维的百分比时，爆炸性剥落发生在300℃。超高性能混凝土（UHPC）的设计强度为150 MPa和1.5 Vol。钢纤维的百分比也显示出300℃的剧烈剥落。本研究中发现的实验结果可以有助于更好地了解在火灾中的HPC和UHPC的行为以及钢纤维对耐火性的作用。
8. Experimental Method for Measuring Solubilities of Heavy Fossil-Fuel Fractions in Compressed Gases to 100 Bar and 300 exp 0 C [R] . Monge, A., Prausnitz, J. M. 1981

机译：测量压缩气体中重化石燃料馏分溶解度为100 Bar和300 exp 0 C的实验方法

The Solubility of MoO_3 in Aqueous Solutions of HClO_4 at T= 300℃ and P = 100 bar by Experimental Data

摘要

著录项

相似文献

相关主题

期刊订阅