Photocatalytic degradation of particulate pollutants and self-cleaning performance of TiO_2-containing silicate coating and mortar

摘要

Photocatalytic degradation of particulate pollutants and self-cleaning performance of TiO_2-containing silicate coatings and TiO_2-containing mortars were experimentally examined and compared using rhoda-mine B (RhB) as a surrogate for airborne particulate pollutants. An optimal dosage of the TiO_2 in the silicate coating was determined from the experiments. The specimens coated with silicate containing 15% TiO_2 by mass of solid silicate had photocatalytic performance comparable to the mortar specimens with 2% TiO_2 by mass of cement although the former required 20 times less TiO_2 (based on 12 mm thick specimens). The specimens coated with silicate containing 15% TiO_2 showed satisfactory degradation efficiency in laboratory accelerated tests up to 2500 h of simulated UV irradiation, similar to at least 2.4 years based on a tropical warm and humid condition, indicating its durable performance.