Studies on the solidification mechanisms of Ni and Cd in cement clinker during cement kiln co-processing of hazardous wastes

摘要

To clarify the solidification mechanisms of heavy metals in cement clinker during the cement kiln co-processing of hazardous wastes, cement clinker samples were produced. EPMA and XANES spectroscopy were employed to acquire information on the microstructure and the Cd and Ni species formed in the cement system. The average Cd concentrations in CaO, C_4AF~3 and C_3S~4 were 3.92%, 1.21% and 0.75%, respectively, but Cd was mostly present in C_3S in clinker (71.0%). The solidification methods of Cd during the calcination process included the formation of a Ca-Cd-0 sosoloid, substitution for Ca in C_3S and C_4AF (isomorphous replacement) and inter the space of the lattice (interstitial solid solution). Ni was combined mainly with Mg in the form of a new Ni-Mg compound (distribution ratio of 61.2%), which was MgNiO_2, as confirmed by XANES analysis. Ni was also present in C_3S and C_4AF (distribution ratios of 24.9% and 10.3%, respectively) by replacement of Ca~(2+) in C_3S and substituting Fe in C_4AF (isomorphous replacement), and also by inter the spaces of the C_4AF lattice (interstitial solid solution).