シリカフユームおよび微細繊維を混入したポーラスコンクリートの耐凍害性と植物の生長

摘要

Porous concrete is expected as an environmental preservation-type concrete but causes concern about its low freeze-thaw resistance compared with that of normal concrete. The purpose of this study is to clarify the effect of silica fume and fine fibers, a new material, on the freeze-thaw resistance of porous concrete. This study also included a vegetation experiment on porous concretes of the same kinds to observe the growth of plants. As a result, the freeze-thaw resistance of porous concrete was significantly improved when 10-30% silica fume and 1 Vol% fibers were used, with large differences in the state of deterioration and number of cracks being observed between normal porous concrete and fiber reinforced porous concrete containing silica fume. The growth of plants on fiber reinforced porous concrete was found to be comparable to that on normal porous concrete.%ポーラスコンクリート（以下PoCと記す）は，環境保全型コンクリートとしてその利用が期待されている。しかし ながら，一般のコンクリートに比べて耐凍害性が低いことが懸念されている。そこで本研究は，シリカフェームおよび新 素材である微細な短繊維を同時に混入した補強PoCを作製も，耐凍害性の向上を目的として実験をおこなった。また， 同種の供試体を用いて植生試験を実施し，植物の生長を観察した。本研究の結果から，シリカフユーム10～30％，繊 維1Vol％を同時に複合使用することによりPoCの耐凍害性が向上することがわかった。また，普通PoCと補強PoCでは劣化状況やひび割れの発生数に大きな違いを生じていることが明らかとなった。さらに，植生実験の結果から，植 物は植生基盤が補強PoCでも普通PoCと同様に生長することがわかった。