塩化物環境下におけるスケーリング抵抗性の評価試騳法に関する基礱的研究

摘要

In Japan, several different test methods, correspondingly applying either the test method regulated in foreign countries or the originally proposed method, have been used to evaluate scaling resistance of concrete according to a researcher's convenience. In this study, the influences in testing conditions exerting the occurrence of scaling were examined using ASTM C672 method and RILEM CDF method. Between both test methods, there existed the differences of the mass of scaled-off particles and the coefficient of variations. Also, the ways how to apply the chloride solution in test, resulted in the change of the amount of scaling. It was confirmed, from the viewpoint of scaling rate, the total mass of scaled-off particles due to change of the water cement ratio and the test method were found to be almost governed by the amount of scaling developed at the early cycle of the freeze-thaw test.%我が国では，スケーリング抵抗性の評価試験法として，海外規格を準用した方法や独自設定した方法が混在し ており，基準となる方法は定められていない。そこで本研究では，我が国で準用される海外規格からASTM C672法 およびRILEM CDF法を対象とし，各々の試験方法の相違がスケーリングの発生性状に及ぼす影響について検討を行 った。その結果，両試験法におりるスケーリング量およびその変動係数には相違が生じることが確認され，主にスケ ーリング量の相違には，試験溶液の供給方法の違いが大きく影響することが示唆された。また，スケーリング速度の 経時的推移について検討した結果，再試験法間に生じるスケーリング量の相違や水セメント比毎に生じるスケーリン グ量の相違は，概ね凍結融解試験開始初期のスケーリングの発生量に支配される様相が認められた。