Plasticity properties of thermally modified timber in bending - The effect of chemical changes during modification of European oak and Norway spruce

摘要

The plasticity of thermally modified European oak (Quercus robur L.) and f thermally modified Norway spruce (Picea abies Karst. (L.)) timber was evaluated in bending, and the plastic properties were related to the changes in chemical composition of the wood after modification. The objective was to gain new knowledge about the properties of materials in the plastic region of the force-deformation diagram in bending. A new software was developed (MATESS) and used to identify important characteristics of the material. This software eliminates shortcomings in current standards, such as simplifications in the evaluation of data when sufficiently sensitive measuring equipment is not available. The characteristics studied were: modulus of rupture (MOR), plastic potential (P-P) chord modulus (CHM), the moduli of plasticity (E-E), and the moduli of plasticity (E-MV, E-P). Extractives, lignin, cellulose, holocellulose, and hemicelluloses were analysed chemically to reveal the patterns that occur during the loading of the specimens. Thermal modification has different effects on the mechanical properties of oak and spruce, especially on CHM, E-MV and E-P, due to their different contents and structures of their chemical components. A strong correlation (r 0.90) between hemicellulose content and MOR and Pp values was found for both species. The coefficients of determination indicated a very low dependence (r(2) 0.1) of MOR, P-p, CHM, E-E, E-MV and E-P, on the average density.