Near tip damage and subcritical crack growth in a particulate composite material

摘要

In this study, pre-cracked sheet specimens were used to conduct constant displacement rate crack propagation tests at room temperature. The effects of microstructure on damage accumulation and fracture processes near the crack tip and crack growth behavior were investigated and the results are discussed.