The results of studies of the influence of chemical-mineralogical composition of the limestone on the properties of the fresh and hardened pastes of the blended alkali-activated slag cements activated by alkaline waste ОАО «Nizhnekamskneftekhim» are presented. The possibility of the blast furnace slag replacement by limestone up to 60 % and improvement of the compressive strength up to 48,8 %. The reinforcing effect increases with the content of calcite in the composition of limestone. Based on the results of studies by X-ray diffraction, scanning election microscopy it is stated that limestone is effective «physically active» for alkali-activated slag cements, which does not form hydration products with binding properties, but positively effects on the microstructure and strength of the blended cement.%Приведены результаты исследований влияния химико-минералогического состава известняка на свойства теста и камня композиционного шлакощелочного вяжущего, активированного щелочным отходом ОАО «Нижнекамскнефтехим». Показана возможность замены шлака молотым известняком до 60 % и увеличения прочностных характеристик камня композиционною шлакощелочного вяжущего до 48,8 %. Упрочняющий эффект добавок возрастает с увеличением содержания кальцита в составе известняка. На основании результатов исследований методами рентгено-фазового анализа, сканирующей электронной микроскопии установлено, что известняк - эффективная «физически активная» добавка к шлакощелочным вяжущим, которая не образует соединений с вяжущими свойствами, но положительно влияет на прочность и микроструктуру камня композиционного вяжущего.
展开▼