Effects of pre-existing interfacial defects on the structural evolution of alumina coated Si electrode during delithiation

Feng Chen; Shi Tielin; Li Junjie; Cheng Siyi; Liao Guanglan; Tang Zirong

首页> 外文期刊>Applied Surface Science >Effects of pre-existing interfacial defects on the structural evolution of alumina coated Si electrode during delithiation

【24h】

Effects of pre-existing interfacial defects on the structural evolution of alumina coated Si electrode during delithiation

机译：预先存在的界面缺陷对铝氧化铝涂覆Si电极结构演变的影响

获取原文

获取原文并翻译 | 示例

获取外文期刊封面封底 >>

开具论文收录证明 >>

文献代查 >>

团队文献服务 >>

页面导航

著录项
引文网络
相似文献
相关主题

著录项

来源
《Applied Surface Science》 |2020年第1期|146366.1-146366.8|共8页
作者
Feng Chen; Shi Tielin; Li Junjie; Cheng Siyi; Liao Guanglan; Tang Zirong;
展开▼
作者单位

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China;

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China|Huazhong Univ Sci & Technol Wuhan Natl Lab Optoelect Wuhan 430074 Peoples R China;

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China;

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China;

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China|Huazhong Univ Sci & Technol Wuhan Natl Lab Optoelect Wuhan 430074 Peoples R China;

Huazhong Univ Sci & Technol State Key Lab Digital Mfg Equipment & Technol Wuhan 430074 Peoples R China|Huazhong Univ Sci & Technol Wuhan Natl Lab Optoelect Wuhan 430074 Peoples R China;

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类
关键词

相似文献

外文文献
中文文献
专利

1. Correlation of interfacial electrode potential and corrosion resistance of plasma polymer coated galvanized steel. Part 2: Influence of forming induced defects [J] . T. Titz, F. Hoerzenberger, K. Van den Bergh, Corrosion science . 2010,第2期

机译：等离子体聚合物涂覆的镀锌钢的界面电极电位与耐蚀性的关系。第2部分：形成缺陷的影响
2. Exposition of sol-gel alumina-coated P92 steel to flue gas: Time-resolved microstructure evolution, defect tolerance, and repairing of the coating [J] . Wollschlaeger Nicole, Nofz Marianne, Doerfel Ilona, Materials and Corrosion . 2018,第4期

机译：溶胶 - 凝胶涂层P92钢的曝光烟气：时间分辨的微观结构演进，缺陷耐受性和涂层修复
3. The Influences of Interfacial Characteristics and Subsurface Microstructural Evolution on Wear Behavior of Al/A206-5 Pct Alumina Micro/Nano-Composites [J] . Saleh Tahamtan, Ayyoub Halvaee, Masoud Emamy Metallurgical and Materials Transactions B . 2015,第3期

机译：界面特性和表面微观结构演变对Al / A206-5Pct氧化铝微/纳米复合材料磨损行为的影响
4. DEFECT EVOLUTION ON COATED SAMPLES UNDER SEVERE THERMAL TRANSIENTS AND INTERFACIAL CHARACTERIZATION [C] . J.T. Harris, A.E. Segall, D. Robinson, ASME Pressure Vessels and Piping conference . 2012

机译：严重热瞬变和界面特征下涂层样品的缺陷演化
5. Interface characterization and defect evolution of coated samples under thermal and pressure transients. [D] . Harris, Jason T. 2012

机译：热和压力瞬变下涂层样品的界面表征和缺陷演变。
6. An in-situ gas chromatography investigation into the suppression of oxygen gas evolution by coated amorphous cobalt-phosphate nanoparticles on oxide electrode [O] . Jihyeon Gim, Jinju Song, Sungjin Kim, -1

机译：原位气相色谱法研究氧化电极上包覆的无定形磷酸钴钴纳米粒子对氧气逸出的抑制作用
7. Reaction kinetic analysis of damage rate effects on defect structural evolution in Fe–Cu [O] . Yoshiie T., Xu Q., Sato K. 2013

机译：损伤速率对铁铜缺陷结构演变的反应动力学分析
8. Theory of the Interfacial Potential Distribution and Reversible VoltammetricResponse of Electrodes Coated with Electroactive Molecular Films. (Reannouncement with New Availability Information) [R] . Smith, C. P., White, H. S. 1992

机译：电活性分子膜包覆电极的界面电位分布理论和可逆伏安响应。（重新公布新的可用性信息）

Effects of pre-existing interfacial defects on the structural evolution of alumina coated Si electrode during delithiation

著录项

引文网络

相似文献

相关主题

期刊订阅