The properties of gold catalysts precursors adsorbed on the MCM-41 materials modified with Mn and Fe oxides

摘要

Silica mesoporous materials modified with manganese and iron were obtained by the hydrothermal method. Gold was introduced to pure and modified silica materials by the direct hydrothermal and impregnation methods. Nitrogen adsorption/desorption studies evidenced formation of the materials with large total surface area and mesoporous structure. Unmodified silica materials showed regular pore arrangement. The uniform porous structure was distorted in the iron or manganese containing samples. XRD, UV-Vis/DRS spectroscopy and temperature programmed reduction studies revealed changes of the nature of transition metal oxide and gold species on the different preparation stages. The oxide species after drying were strongly dispersed and partially incorporated to the silica framework. High temperature treatment led to the formation of extraframework Mn and Fe oxide species. Complex processes of gold deposition were observed during hydrothermal synthesis and impregnation of modified silica materials. The increase of the size of gold species was observed during calcination. The presence of transition metal oxides decreased sintering of gold crystallites.