EVA热熔胶膜用于环氧树脂类光致聚合物全息存储卡的制备工艺研究

     

摘要

Using EVA hot melt adhesive film, an epoxy resin prepared photopolymer holographic memory card was prepared, and the preparation process is simple. First, prepared epoxy photopolymer temperature tests were conducted and a new process for the preparation of the holographic storage medium has been proposed. Then, its 532 nm wavelength holographic characteristics were studied. The holographic memory card with a high temperature (≥60℃), easy to scratch characteristic diffraction efficiency≥50%, moderate exposure sensitivity, can be angular multiplexing holographic storage. The holographic storage card for long-term storage tests has been conducted and the cartridge shelf life results≥ 6 months have been drawn.%本文采用EVA热熔胶膜,制备了一种环氧树脂类光致聚合物全息存储卡,制备工艺简单。首先对所制备的环氧树脂类光致聚合物进行了耐高温试验,提出了一种新的全息存储介质制备工艺方法;使用532 nm波长激光对制备的全息存储卡进行了全息特性研究。该全息存储卡具有耐高温(≥60℃)、不易划伤特点,衍射效率不低于50%,曝光灵敏度适度,可进行角复用全息存储。经长时间存放试验,得出暗盒存放条件下该全息存储卡的保存期不少于6个月的结果。

著录项

  • 来源
    《光电工程》|2015年第1期|39-44|共6页
  • 作者单位

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

    中国电子科技集团公司第三十三研究所;

    太原 030006;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 全息光学;
  • 关键词

    全息存储; 光致聚合物; 乙烯-醋酸乙烯共聚物;

  • 入库时间 2023-07-25 15:16:00

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号