Achieving high-capacity and long-life K^(+)storage enabled by constructing yolk-shell Sb_(2)S_(3)@N,S-doped carbon nanorod anodes

摘要

As promising anode candidates for potassium-ion batteries(PIBs),antimony sulfide(Sb_(2)S_(3))possesses high specific capacity but suffers from massive volume expansion and sluggish kinetics due to the large K^(+)insertion,resulting in inferior cycling and rate performance.To address these challenges,a yolk-shell structured Sb_(2)S_(3)confined in N,S co-doped hollow carbon nanorod(YS-Sb_(2)S_(3)@NSC)working as a viable anode for PIBs is proposed.As directly verified by in situ transmission electron microscopy(TEM),the buffer space between the Sb_(2)S_(3)core and thin carbon shell can effectively accommodate the large expansion stress of Sb_(2)S_(3)without cracking the shell and the carbon shell can accelerate electron transport and K^(+)diffusion,which plays a significant role in reinforcing the structural stability and facilitating charge transfer.As a result,the YS-Sb_(2)S_(3)@NSC electrode delivers a high reversible K^(+)storage capacity of 594.58 m A h g^(-1)at 0.1 A g^(-1)and a long cycle life with a slight capacity degradation(0.01%per cycle)for 2000 cycles at 1 A g^(-1)while maintaining outstanding rate capability.Importantly,utilizing in in situ/ex situ microscopic and spectroscopic characterizations,the origins of performance enhancement and K^(+)storage mechanism of Sb_(2)S_(3)were clearly elucidated.This work provides valuable insights into the rational design of high-performance and durable transition metal sulfides-based anodes for PIBs.