新型增韧剂对PBT/PC合金增韧的研究

摘要

以双烯烃、苯乙烯、甲基丙烯酸甲酯为单体,采用种子聚合技术,合成了具有核-壳结构的接枝共聚物(MIS树脂),并与PBT/PC合金共混.结果表明,MIS树脂为15～18份时,PBT/PC合金的冲击强度最大.加入MIS树脂后,PBT/PC合金的断层明星,而且出现了很多小空洞,提高了PBT/PC合金的力学性能.MIS树脂可以用做PBT/PC合金的低温增韧剂.%A core-shell structure of graft copolymer(MIS resin) was synthesized with double-olefins, styrene, methyl methacrylate as monomers by using the seed polymerization, and the MBS resin blended with PBT/PC alloy. The results showed that when the MIS resin content were 15-18 parts, the impact strength of the PBT/PC alloy reached the highest.After adding the MIS resin, the chasm of the PBT/PC alloy was obvious, and many small holes appeared, the mechanical properties of the PBT / PC alloy was improved. The MIS resin could be used as PBT/PC alloy toughening agent at low temperature.