Stress Distribution in Maxillary Central Incisors without Ferrules: A Finite Element Analysis of Post and Core Systems

摘要

Purpose: The purpose of this study was to identify optimal post and core materials for central incisors without ferrules using three-dimensional finite element analysis and three-point bending tests. Methods: Stress analyses were performed with six models: cast metal post and core (MP), composite resin core alone, straight fiber-reinforced post-composite resin core (FSR), tapered fiber-reinforced post-composite resin core, straight titanium post-composite resin core (TSR), and tapered titanium post-composite resin core (TTR). A 100-N load was applied to the lingual surface at a 45° angle to the long axis of the tooth. Maximum von Mises stress distributions were calculated with finite element analysis software. Five samples each of composite resin, straight fiber-reinforced post, straight titanium post, straight fiber-reinforced post and composite resin, and straight titanium post and composite resin were subjected to three-point bending tests, followed by analysis of variance and Tukey’s multiple comparison test. Results: Stress distribution was optimal on TTR. Maximum von Mises stress on the cervical side of the post was greatest in TSR (693 MPa) and TTR (556 MPa). Maximum stress on the apical side of the post was greatest in MP (110 MPa). Maximum stress in surrounding dentin was lowest in MP (203 MPa) and TTR (250 MPa). Gap distance was smallest in MP (0.09 mm) and largest in FSR (0.26 mm). Mean maximum three-point bending force was lowest in composite resin (26.9 N/mm) and highest in titanium post and composite resin (97.1 N/mm). Titanium post bending strength was consistently greater than that of the fiber-reinforced post (p Conclusion: These results revealed optimal stress distribution and high bending strength with the tapered titanium post and resin combination, suggesting that this combination can most effectively prevent root or post fracture in an anterior tooth without a ferrule.