The microstructure characteristics and fracture behavior of the polyhedral primary iron-rich phase and plate-shaped eutectic iron-rich phase in a high-pressure die-cast AlSi10MnMg alloy

摘要

The characterization of multiple iron-rich phases in high-pressure die-cast AlSi10MnMg alloy was studied.Attention was focused on the formation and fracture behavior of the primary iron-rich phase((P-IMC)_(I))formed in the shot sleeve and plate-shaped eutectic iron-rich phase in high-pressure die cast(HPDC)AlSi10MnMg alloy.Results show that multiple types of iron-rich phases with various morphologies,in-cluding primary iron-rich phases(polyhedral(P-IMC)_(I) and(P-IMC)_(II))and eutectic iron-rich phases(plate-shaped,net shape,and fish-bone shape),were found in HPDC AlSi10MnMg.Coarse(P-IMC)_(I) formed in the shot sleeve were distributed in the interface between primaryα-Al and binary Al-Si eutectic.Small size(P-IMC)_(II) and various eutectic iron-rich phases formed in the die cavity and they were distributed in Al-Si binary eutectic.The primary iron-rich phases belonged to a simple cubic crystal structure with a lattice constant a=1.265 nm and they exhibited a lateral growth characteristic with a termination of{110}surface.βphase was surrounded byδphase and they coexisted in a plate-shaped iron-rich phase.High-density stacking fault inβphase andδ/βinterface provided an excellent nucleation site forδphase.From mechanical behavior,the stress concentration caused by eutectic iron-rich phases was far less than(P-IMC)_(I) and it would not cause crack initiation along the eutectic cluster boundary.In addition,(P-IMC)_(I) showed the worst deformation coordination with primaryα-Al while the plate-shaped eutectic iron-rich phase exhibited similar deformation characteristics with silicon particles.