Hazard evaluation of ignition sensitivity and explosion severity for three typical MH_(2) (M=Mg,Ti,Zr)of energetic materials

摘要

MgH_(2),TiH_(2),and ZrH_(2) are three typical metal hydrides that have been gradually applied to composite explosives and propellants as additives in recent years.To evaluate ignition sensitivity and explosion severity,the Hartmann device and spherical pressure vessel were used to test ignition energy and explosion pressure,respectively.The results showed that the ignition sensitivity of ZrH_(2),TiH_(2) and MgH_(2) gradually increased.When the concentration of MgH_(2) is 83.0 g/m^(3) in Hartmann device,the ignition energy attained a minimum of 10.0 mJ.The explosion pressure of MgH_(2) were 1.44 times and 1.76 times that of TiH_(2) and ZrH_(2),respectively,and the explosion pressure rising rate were 3.97 times and 9.96 times that of TiH_(2) and ZrH_(2),respectively,through the spherical pressure vessel.It indicated that the reaction reactivity and reaction rate of MgH_(2) were higher than that of TiH_(2) and ZrH_(2).In addition,to conduct in edepth theoretical analysis of ignition sensitivity and explosion severity,gas production and combustion heat per unit mass of ZrH_(2),TiH_(2) and MgH_(2) were tested by mercury manometer and oxygen bomb calorimetry.The experimental results revealed that MgH_(2) had a relatively high gas production per unit mass(5.15 mL/g),while TiH_(2) and ZrH_(2) both had a gas production of less than 2.0 mL/g.Their thermal stability gradually increased,leading to a gradual increase in ignition energy.Furthermore,compared with theoretical combustion heat,the combustion ratio of MgH_(2),TiH_(2) and ZrH_(2) was more than 96.0%,with combustion heat value of 29.96,20.94 and 12.22 MJ/kg,respectively,which was consistent with the explosion pressure and explosion severity test results.