The variation of the friction coefficient of the CuAlBi alloy at different connecting loading and friction speed were investigated by using MMU-5G sliding friction-wear tester, besides, the wear mass loss of the CuAlBi alloy was measured, and the influence of loading and rotation speed on friction and wear properties of CuAlBi alloy was also discussed. The results show that the friction coefficient increase then decrease with increase of connecting loading as well as decreases with increase of friction speed, and the wear loss mass increases with increase of connecting loading and friction speed. As a result, the wear failure form of CuAlBi alloy is mainly ploughing.