Study on the Structures and Properties of Ni-W-B-CeO_2 Composite Coatings Prepared by Pulse Electrodeposition

摘要

The aim of this research is to pulse co-deposit nano-CeO2 particles into Ni-W-B alloy coatings in order to improve the surface properties. The influence of pulse frequency and duty circle on deposition rate, microhardness and microstructures, and the influence of heat treatment temperature on phase structures, microhardness and abrasivity of Ni-W-B-CeO2 composite coatings were investigated. The results indicated that the pulse co-deposition of nickel, tungsten, boron and nano-CeO2 particle from the bath which nano-CeO2 particle was suspended by high speed mechanical stirring led to the Ni-W-B-CeO2 composite coatings, possessing better microhardness and abrasion resistance when heat-treated at 400 ℃ for 1 h. The microhardness as-deposited with 636 Hz and the deposition rate with 0.0281 mm·h-1 was the highest at pulse frequency with 1000 Hz and pulse duty circle with 10%. Microstructures analysis displays that decreasing pulse duty cycle leads to refinement in grain structures and the improvement of microstructures. X-ray diffraction shows that the composite coating as-deposited was mainly in the amorphous state and partially crystallized, but when heat treated at 400 ℃, the crystallization trend was strengthened further.