Luminescent material Ba3Gd(BO3)3 doped with Eu3+ ion was prepared by high temperature solid-state method.The preparing conditions, luminescent properties, and particle morphology of Ba3Gd(BO3)3:Eu3 + phosphor were studied with X-ray diffraction(XRD), fluorescence spectroscopy, and scanning electron microscopy(SEM).The results obtained by XRD showed that pure phase of Ba3Gd(BO3)3 was obtained at 1000 °C.Images from SEM displayed that the particles of Ba3Gd(BO3)3:Eu3+ phosphor had a spherical shape with an average diameter of about 200-400 nm.The luminescence spectra showed that Ba3Gd(BO3)3:Eu3+ phosphor was effectively excited by the near ultraviolet(UV) light(396 nm) and blue light(466 nm).The main emission peaks of Ba3Gd(BO3)3:Eu3+ phosphor were assigned to the supersensitive transition 5D0-7F2(611 and 616 nm) of Eu3+ ion when samples were excited at 255 and 396 nm, respectively, and the luminescent intensity of Ba3Gd(BO3)3:Eu3+ at 611 and 616 nm reached to the maximum when the doped content of Eu3+ ion was 10mol.%.Therefore, this phosphor could be a promising red component for possible applications in the field of white LED.
展开▼