The method for preparing yttrium oxide with large specific surface area was introduced. By means of BET, SEM, TG and DTA analysis, the effects of precipitant, stirring velocity, non-RE impurity in solution, calcination temperature, on the surface area were studied respectively. The Y2O3 sample with specific surface area of more than 60 m2·g-1 and L.O.I less than 1% was prepared in the suitable precipitation condition and calcinations temperature when the ammonia used as precipitant. The SEM shows that the Y2O3 prepared with large surface area is the aggregation of about 50 nm particles.