Microstructure comparison of ZK60 alloy under casting,twin roll casting and hot compression

摘要

The microstructures of ZK60 alloy under conventional direct as-casting (DC),twin roll casting (TRC) and twin roll casting followed by hot compression (TRC-HC) were analyzed by optical morphology (OM),electron backscatter diffraction (EBSD) and X-ray diffraction (XRD).The deformation condition of hot compression is 350 ℃,0.1 s?1.The microstructural evolution under TRC-HC deformation followed by annealing at different temperatures and time was discussed.The results show that TRC provides more modified microstructure compared with DC.Twins are found in TRC processing;dynamic recrystallization (DRX),shear bands and twins are found in TRC-HC.A short annealing time has little effect on hardness,while during a long time annealing,it is found that low annealing temperatures increase the micro-hardness and high temperature decreases it.