Innovative hydrophobic/hydrophilic perfluoropolyether(PFPE)/polyvinylidene fluoride(PVDF)composite membrane for vacuum membrane distillation

摘要

Though membrane distillation(MD)has gained more and more attention in the field of desalination,the wetting phenomenon was still a non-negligible problem.In this work,a method combined dip-coating and UV in situ polymerization for preparing hydrophobic/hydrophilic perfluoropolyether(PFPE)/polyvinylidene fluoride composite membranes.This composite membrane consisted of a top thin hydrophobic coating layer and hydrophilic substrate membrane.In terms of anti-wetting properties,contact angle and liquid entry pressure of all composite membranes(except for those based on 0.45μm)exceeded 160°and 0.3 MPa,respectively.In particular,the desalination performance was tested in vacuum membrane distillation tests by feeding 3.5%(mass)saline solution(NaCl)at 60℃.The composite membranes with larger support pore size and lower PFPE content had higher membrane distillation flux.And for stability tests(testing the 0.22μm membrane coated by 5%(mass)PFPE),the highest MD flux29.08 kg·m^(-2)·h^(-1) and stable salt rejection(over 99.99%)during the period.Except that,the effects of coating material concentration and pore sizes of substrate membrane were also investigated for surface morphology and topography,porosity,mechanical strength and pore size characteristics.This work provided a simple and effective alternative to prepare excellent hydrophobic composite membranes for MD applications.