(1-x)K_(0.5)Na_(0.5)NbO_3-xLiBiO_3无铅压电陶瓷的结构与压电性能(英文)

摘要

采用传统固相反应制备了(1-x)(K0.5Na0.5)NbO3–xLiBiO3[(1–x)KNN–xLB](x=0,0.0005,0.001,0.002,0.004,0.006,0.008,0.010)压电陶瓷,并分析研究了其微结构及电性能。结果表明,LB 掺杂的 KNN 陶瓷主要形成了钙钛矿结构,没有检测到第二相的存在,并且陶瓷的相结构出现直接由正交相过渡到立方相的"反常"转变;随着LB 掺杂量的增加,晶粒尺寸逐渐细化,陶瓷的压电常数d33、平面机电耦合系数kp先略有增加后显著下降,且分别在x=0.002和 x=0.001时达到最大值,分别为115pC/N和0.2701;陶瓷的介电常数εr随x增大先增加后略有降低,当 x=0.006时获得最大值,为871.8。