Crystallization behavior of amorphous Zr_(70)Cu_(20)Ni_(10) alloy annealed at 380 ℃

摘要

Crystallization behavior of amorphous Zr 70 Cu 20 Ni 10 alloy isothermally annealed at 380 ℃ was first investigated by employing the differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). It has been found that an exothermic peak appears in the DSC trace when the annealing time is about 17～18 min, indicating a certain phase transformation occurs in the matrix of amorphous Zr 70 Cu 20 Ni 10 alloy. Meanwhile, isothermal annealing experiments for amorphous Zr 70 Cu 20 Ni 10 alloy ranging from 360 ℃ to 400 ℃ with a temperature interval of 10 ℃ were also carried out, from which no exothermic reaction can be observed except for the case of 380 ℃. This behavior indicates that the phase transformation during isothermal annealing of amorphous Zr 70 Cu 20 Ni 10 alloy is strongly temperature and time dependent. Further investigations are required to reveal the nature of such phenomenon.