首页> 中文期刊>化学研究 >ZnO/CNTs复合材料吸附脱除H2S的性能研究

ZnO/CNTs复合材料吸附脱除H2S的性能研究

     

摘要

采用热分解法制备ZnO/CNTs复合材料,通过傅立叶变换红外光谱(FT-IR)、X射线衍射(XRD)、透射电镜(TEM)、扫描电镜(SEM)和N2吸脱附测试分别表征样品的结构、形貌特征及比表面积,并使用固定床反应器测试其吸附脱硫性能.结果表明,制备的ZnO/CNTs具有吸附脱除H2 S能力物质为ZnO,当ZnO的负载量为0.5%时,穿透时间可达到185 min,穿透硫容最高.%ZnO/carbon nano-tubes ( CNTs) composites were prepared by thermal decomposition meth-od. The structure, morphology and specific surface area of the samples were characterized by Fourier transform infrared spectroscopy ( FT-IR) , X-ray diffraction ( XRD) , transmission electron microscopy (TEM), scanning electron microscopy (SEM) and N2 desorption, and the adsorption desulfurization performance was measured using a fixed bed reactor. The results show that the prepared ZnO/CNTs has the ability to remove H2 S by ZnO. When the loading of ZnO was 0.5%, the penetration time was up to 185 min with the highest sulfur mass content.

著录项

  • 来源
    《化学研究》|2017年第5期|612-616|共5页
  • 作者单位

    河南大学 化学化工学院,河南 开封475004;

    河南尉氏县盐业管理局,河南 尉氏475500;

    河南大学 化学化工学院,河南 开封475004;

    河南大学 化学化工学院,河南 开封475004;

    河南省废弃物资源能源化工程技术研究中心,河南大学,河南 开封475004;

    河南大学 化学化工学院,河南 开封475004;

    河南省废弃物资源能源化工程技术研究中心,河南大学,河南 开封475004;

    河南大学 化学化工学院,河南 开封475004;

    河南省废弃物资源能源化工程技术研究中心,河南大学,河南 开封475004;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 金属元素及其化合物;
  • 关键词

    氧化锌; 碳纳米管; 复合材料; 脱硫;

  • 入库时间 2023-07-25 21:25:57

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号