铌镁酸铅-钛酸铅陶瓷由于其优异的性能而有着广泛的应用．采用两步法制备了组分为0.9Pb（Mg2/3Nb1/3）O3-0.1PbTiO3（0.9PMN-0.1PT）的弛豫铁电陶瓷，并对其介电-温度特性和热释电特性等进行了研究．结果表明，0.9PM N-0.1PT 陶瓷介电-温度曲线服从 Uchino和 No-mural改进的居里-外斯定理，表现出很强的介电弛豫特性，介电峰明显宽化，频率色散强烈，峰值温度 Tm 随频率增大向高温移动，弛豫因子达到1.89．热释电流密度曲线平缓，在整个加热范围均有电荷释放，室温时热释电系数达到100 pC · m -2 K -1．%The lead magnesium niobate-lead titanate ceramics are extensively use due to their excellent di-electric properties .The relaxor ferroelectricceramic 0.9Pb(Mg2/3Nb1/3)O3-0.1PbTiO3(0.9PMN-0.1PT) was fabricated through two steps method .The dielectric properties ,dielectric constant and loss depend-ent on temperature ,pyroelectric ,were experimentally investigated .The results show that the dielectric constant-temperature curve obey the modified C-W law by Uchino and Nomural .The 0.9PMN-0.1PT ceramic reveal strong dielectric relaxor behavior ,wide dielectric peak ,strong frequency dispersion ,and the peak temperature Tm shift to higher with the frequency increasing ,the relaxor factor is 1 .89 .The py-roelectric curve change slowly and continuously release charges during whole heating process .The pyroe-lectric coefficient is 100pC · m -2 K -1 inroom temperature .
展开▼