首页> 外文学位 >Stress corrosion cracking and internal oxidation of alloy 600 in high temperature hydrogenated steam and water

【24h】

Stress corrosion cracking and internal oxidation of alloy 600 in high temperature hydrogenated steam and water

机译：高温氢化蒸汽和水中合金600的应力腐蚀开裂和内部氧化

获取原文

获取原文并翻译 | 示例

页面导航

著录项
相似文献
相关主题

著录项

作者
Lindsay, John.;
展开▼
作者单位

The University of Manchester (United Kingdom).;

展开▼
授予单位 The University of Manchester (United Kingdom).;
学科
学位 Ph.D.
年度 2015
页码 260 p.
总页数 260
原文格式 PDF
正文语种 eng
中图分类
关键词
入库时间 2022-08-17 11:59:58

相似文献

外文文献
中文文献
专利

1. Evaluation of Primary Water Stress Corrosion Cracking Resistance of Three Heats of Alloy 600 in 400 °C Hydrogenated Steam Condition [J] . Eunsub Yun, Hansub Chung, Changheui Jang Metals . 2018,第2期

机译：在400°C氢化蒸汽条件下三种合金600热对一次水应力腐蚀抗裂性的评价。
2. Grain boundary selective oxidation and intergranular stress corrosion crack growth of high-purity nickel binary alloys in high-temperature hydrogenated water [J] . Bruemmer S. M., Olszta M. J., Toloczko M. B., Corrosion science . 2018,第feba期

机译：高温氢化水中高纯镍二元合金的晶界选择性氧化和晶间应力腐蚀裂纹扩展
3. Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water [J] . Moss Tyler, Was Gary S. Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science . 2017,第4期

机译：氢化超临界水中合金600和690的加速应力腐蚀裂纹启动
4. Characterisation of Stress Corrosion Cracking and Internal Oxidation of Alloy 600 in High Temperature Hydrogenated Steam [C] . J. Lindsay, F. Scenini, X. Zhou, International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors . 2016

机译：高温氢化蒸汽中合金600应力腐蚀裂纹和内氧化的特征
5. Oxidation products of Inconel alloys 600 and 690 in hydrogenated steam environments and their role in stress corrosion cracking. [D] . Ferguson, J. Bryce. 2006

机译：Inconel合金600和690在氢化蒸汽环境中的氧化产物及其在应力腐蚀开裂中的作用。
6. Stress Corrosion Cracking Behavior of Alloy 600 Coupled to Magnetite under High-Temperature Caustic Conditions [O] . Geun Dong Song, Jeoh Han, Soon-Hyeok Jeon, 2019

机译：高温苛性条件下耦合磁铁矿的600合金的应力腐蚀开裂行为
7. Surface Finishing Effect on Stress Corrosion Cracking Test Results of Alloy 600 by Uni-Axial Constant Load Test in Hydrogenated Steam Environment [O] . Yohei Sakakibara, Ippei Shinozaki, Gen Nakayama 2017

机译：氢化蒸汽环境中的单轴恒定载荷试验对合金600应力腐蚀裂纹试验结果的表面整理效果
8. Stress Corrosion Cracking of Alloy 600 and Alloy 690 in All Volatile Treated Water at Elevated Temperatures. Final Report (PWR) [R] . Theus, G. J., Emanuelson, R. H. 1983

机译：高温下所有挥发性处理水中合金600和合金690的应力腐蚀开裂。最终报告（pWR）

Stress corrosion cracking and internal oxidation of alloy 600 in high temperature hydrogenated steam and water