首页> 外文学位 >A study of hydrogen enrichment at pits and other surface discontinuities in mild steel and the contribution to near-neutral pH stress corrosion cracking

【24h】

A study of hydrogen enrichment at pits and other surface discontinuities in mild steel and the contribution to near-neutral pH stress corrosion cracking

机译：研究低碳钢凹坑和其他表面不连续处的氢富集及其对近中性pH应力腐蚀开裂的影响

获取原文

获取原文并翻译 | 示例

页面导航

著录项
相似文献
相关主题

著录项

作者
Wall, Laura;
展开▼
作者单位

University of Alberta (Canada);

展开▼
授予单位 University of Alberta (Canada);
学科
学位 M.Sc.
年度 2007
页码 191 p.
总页数 191
原文格式 PDF
正文语种 eng
中图分类
关键词
入库时间 2022-08-17 11:55:22

相似文献

外文文献
中文文献
专利

1. Influence of inclusions on initiation of pitting corrosion and stress corrosion cracking of X70 steel in near-neutral pH environment [J] . Wang Liwei, Xin Juncheng, Cheng Lianjun, Corrosion science . 2019,第FEBa期

机译：夹杂物对近中性pH环境下X70钢点蚀和应力腐蚀开裂的影响
2. Application of inverse Broyden'S method for computational analysis of hydrogen contribution to the near-neutral pH stress corrosion cracking [J] . Telichev I., Vinogradov O. International journal of computational methods . 2013,第5期

机译：逆Broyden法在氢对近中性pH应力腐蚀裂纹贡献的计算分析中的应用。
3. Hydrogen in stress corrosion cracking of X-70 pipeline steels in near-neutral pH solutions [J] . Fang BY, Han EH, Wang JQ, Journal of Materials Science . 2006,第6期

机译：X-70管线钢在近中性pH溶液中的应力腐蚀开裂中的氢
4. CORROSION FATIGUE AND NEAR-NEUTRAL pH STRESS CORROSION CRACKING OF PIPELINE STEEL IN VERY DILUTE CARBONATE/BICARBONATE WITH AND WITHOUT THE PRESENCE OF HYDROGEN SULFIDE USING THE COMPLIANCE TECHNIQUE [C] . R.L. Eadie, K.E. Szklarz, R.L. Sutherby NACE annual conference exposition . 2003

机译：使用顺应性技术非常稀释碳酸盐/碳酸氢盐的管道钢的腐蚀疲劳和近中性pH应激腐蚀破裂耐硫化物的存在
5. Mechanistic studies on stress corrosion cracking of pipeline steels in near-neutral pH environments. [D] . Gu, Biao. 2000

机译：在接近中性pH的环境中对管线钢进行应力腐蚀开裂的机理研究。
6. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对X70管线钢在近中性pH环境下点蚀和应力腐蚀开裂行为的综合影响
7. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对近中性pH环境中X70管道钢蚀腐蚀和应力腐蚀开裂行为的综合作用

A study of hydrogen enrichment at pits and other surface discontinuities in mild steel and the contribution to near-neutral pH stress corrosion cracking

著录项

相似文献

相关主题

期刊订阅