Through-thickness inhomogeneity of steel-sheet texture and its effect on material properties.

摘要

The work of this thesis centres around two related themes, the first being the characterization of the through-thickness inhomogeneity found in rolled sheet at various stages in its production. The second is involved with attempting to understand how and to what extent the existing inhomogeneity affects the correlations with the anisotropies of some physical or mechanical properties. For this, the inhomogeneity of six steels were measured.;To contrast the extensive inhomogeneity expected in the ferrosilicon steels, the remaining three steels consisted of two continuous-annealed, interstitial-free, extra-low-carbon steels and one aluminum-killed, batch-annealed, low-carbon steel, all three of which are commercial final product, deep drawing steels. (Abstract shortened by UMI.).;Three were specimens removed from the sheet during the early processing of conventional grain-oriented ferrosilicon steel, one sample taken after the first cold rolling stage, another taken after the intermediate anneal, while the last was taken after the following stage, i.e. after the second cold rolling.