Sulfate induced accelerated corrosion of low carbon steel in chlorine-contaminated environments.

摘要

The effects of the temperature, amount of the mixed salt, potentials of oxygen, sulfur oxides (SO;When the water vapor is added to the dry gas mixture containing HCl, the chlorine potential decreased to 3.8 ;The maximum corrosion rate was observed at 600;Sulfate induced accelerated attack of 0.1% carbon steel in mixed 2% O