Synthesis, characterization, and catalytic activity of type 2 crystalline titanates prepared with supercritical drying.

摘要

Supercritically dried silico-alumino-titanate (Si-Al-Ti) mixed oxides (T2CT) were successfully synthesized by a sol-gel method with hydrothermal synthesis temperatures less than 200°C and autogenic pressure. High-surface-area T2CT aerogels with meso- to macroporosity were obtained. All solid products, after calcination at 450°C, are semicrystalline. In addition, successful scale-up of T2CT synthesis in a one-gallon reactor yielding 500 g was achieved.; Surface areas, pore volumes, and average pore diameters are greatly influenced by the drying method. Supercritical drying had no effect on the crystalline or molecular structure of the materials. The synthesized materials were characterized by means of nitrogen physisorption, X-ray diffraction (XRD), thermal analysis, and diffuse reflectance FTIR spectroscopy. The addition of different amounts of phosphorous and antimony affected neither the textural nor the structural aspects of T2CT. However, a decrease in surface area occurred.; The catalytic activity of these materials was evaluated after being loaded with nickel and molybdenum by the incipient wetness method. Cyclohexene hydrogenation and thiophene hydrodesulfurization reactions are used in the catalytic activity study. The activities of some of the catalyst prepared in this study are in the same range as the commercial catalyst, Shell 324, but with lower metal loadings than the commercial catalysts. Thus, more efficient use of Mo and Ni was observed.