7Li NMR study of ionically conducting glasses

摘要

Temperature dependence of 7Li NMR was measured in 50Li_2O-50B_2O_3 glasses. A new method for the analysis of motional narrowing of the line width incorporating kohlrasuch-Williams-Watt function, exp is presented. The obtained activation parameters are compared with that from conductivity. It was shown that MNLW can be explained by the same activation energy from conductivity. It was found that electrical relaxation time was an order of magnitude smaller than that from those from NMR line width. At high tmeperature region, where the line is well narrowed, a residual line width was obseved .It is as large as 1kHz, and gradually decreases with the increase in temperature. It was explained that there is a mobility difference in lithium ions in this glass. These results suggest that some fraction of ions are highly mobilized in the glass.