Corrosion Behavior of TP95S Anti-sulfur Casing Steel in High Temperature High Pressure H_2S/CO_2 Environment

摘要

The anti-corrosion performance of Tiangang TP95S casing steel was studied by high temperature autoclaves simulating the high-temperature and high-pressure H_2S/CO_2 environment. The experimental results show that the corrosion rates increase with the rising of temperature which is from 40°C to 80°C under the dynamic and static conditions of the simulated environments; the dynamic corrosion rates are between 1.7294 and 1.8601mm/a and the corrosion rates are 0.4264～1.2715mm/a under the static conditions, both of which belong to a serious corrosion category; the dynamic corrosion samples have had the localized corrosion at 40°C, but the local corrosion of the static corrosion specimens appeared at 80°C; the corrosion product of TP95S steel takes FeS as the core in the case of static corrosion at 40°C.