The Influence of Chemical Composition of Aliphatic-Aromatic Copolyesters on Their Properties

摘要

The chain microstructure and properties of a series of aliphatic-aromatic copolyesters in a range of compositions from 10 to 100% of aromatic components were studied by examining melting and crystallization behaviors, dynamic mechanical response, morphology, wide- (WAXS) and small-angle X-ray scattering (SAXS), and tensile deformation. Chain microstructure was analyzed by ~1H NMR. The results indicate that most of copolyesters used in this study have essentially random distribution of comonomers. Copolyesters with more than 30 mol% of aromatic part crystallize with a crystal structure characteristic for homopolymer poly(butylene terephthalate) (PBT). However, some of the reflections from crystal planes are shifted towards lower diffraction angles as compared to butylene terephthalate homoplymer. The phase transition temperatures decrease with increasing aliphatic content. By means of polarized light microscopy (PLM), small-angle light scattering (SALS) and SAXS, crystallization behavior of a selected aliphaticaromatic copolyester was further explored. Selected copolyester crystallizes in the form of thin fibrous crystals, few nanometers thick, which is the main factor influencing the depression of its melting temperature.