The Physical Characteristics of Electrorefined Copper Starter Sheet Material

摘要

The interaction of anode and electrolyte chemistry in copper electrore-fining is complex. This is especially true with regard to the behavior of Group 15 elements (As, Sb, and Bi). To better understand this system, laboratory electrore-fining experiments were conducted using commercial anodes with As/(Sb + Bi) molar ratios of 0.54 and 3.8 and an electrolyte collected from a commercial refinery. The effect of adding thiourea during plating was also examined. Twenty-one hour copper deposits were produced in the laboratory to simulate starter sheet production. The mechanical properties of the electrodeposited copper as measured by an industrially relevant empirical bend test and a one-point bend test developed by UFMG are reported. The crystal structures of the samples were also examined.